Độ chịu lửa (Bằng)
Common (1580 ° <Độ chịu lửa <1770 °)
Raw material
Sintered Magnesia
Compressive strength 110°C
62MPa
Compressive strength 1000°C
54MPa
Reheating linear change
-0.15%(1600°C)
Feature
Good volume stability at high temperature
Application
for Induction Furnace/EAF/electric arc furnaces/tundish